3D Printers Pyrex Glass High Borosilicate Glass Plates 3.3

• Customization: Available
• After-sales Service: 1 Years
• Type: Refractory Glass
• Model NO.: BG-P11
• Structure: Solid
• Function: Optical Function, Biological and Chemical Function
• Transparency: Transparent
• Color: Clear
• Usage: Furniture, Door, Building, Window, Microwave Oven
• Thickness: 2-25mm
• Length: >1650mm
• Width: 1650mm
• Expansion Coefficient: 3.25
• Size: Custom
• Transport Package: Wooden Crate/Carton /Customized Package
• Specification: ISO9001, CCC
• Trademark: bolipai
• Origin: Guangdong China
• Production Capacity: 20000PCS/Month

Product Description

                          

Factory production of high borosilicate glass high borosilicate heat-resistant glass
 borosilicate glass high temperature resistance high level

 

China is the third country that can produce float high borosilicate glass 3.3. plat borosilicate glass 3.3 (English name: plat borosilicate glass 3.3, alternative to SCHOTT trademark borofloat ® 3.3,CORNING trademark pyrex ®7740) is manufactured by float process. A flat glass with sodium oxide (Na2O), boron oxide (B2O3) and silicon dioxide (SiO2) as the basic ingredients. The content of boron and silicon in this kind of glass is high, boron: 12.5 ~ 13.5%, silicon: 78 ~ 80%. So this kind of glass is called high borosilicate glass. It belongs to Pylex glass in borosilicate glass. It is characterized by small coefficient of thermal expansion, good thermal stability, chemical stability, light transmittance and electrical properties, so it has chemical erosion resistance, thermal impact resistance, good mechanical properties, high temperature, high hardness characteristics, so it is also known as heat-resistant glass, heat-resistant impact glass, high temperature resistant glass, but also a kind of special fireproof glass.

Specifications
1. Excellent visual effect
2. Powerful effect on Fire, hydrolysis and Chemical Resistance
3. High resistance to thermal shock.
BOROSILICATE FLOAT GLASS DESCRIPTION
Borosilicate glass has a very low thermal expansion coefficient, about one-third that of ordinary glass. This reduces material stresses caused by temperature gradients, thus making it more resistant to breaking. This makes it a popular material for objects like telescope mirrors, where it is essential to have very little deviation in shape. It is also used in the processing of high-level nuclear waste, where the waste is immobilised in the glass through a process known as vitrification (contrast with Synroc).


BOROSILICATE FLOAT GLASS 3.3 

1. Household electrical appliance (panel for oven and fireplace, microwave tray etc. );
2. Environmental engineering and chemical engineering (Lining layer of repellence, autoclave of chemical reaction and safety spectacles);
3. Lighting (spotlight and protective glass for jumbo power of floodlight);
4. Power regeneration by solar energy (solar cell base plate);
5. Fine instruments (optical filter);
6. Semi-conductor technology (LCD disc, display glass);
7. Iatrology and bio-engineering;

Mechanical   properties
Density (g/cm3) (at 25°C)	2.23±0.02
Knoop hardness	480
Flexure   strength	24Mpa
Thermodynamic   properties
Coefficient   of   thermal   expansion (α) (0-300°C)	3.3±0.1×10-6
Softening point (°C)	830±10
Strain   point  (°C)	521±10
Specific   heat   capacity	(2-100°C)0.83KJ×(kg×K)-1
Thermal conductivity	1.2W×(m×k)-1
Thermal shock resistance(K)	300
Temperature performance(K)	200
Maximum   working   temperature	(>10h, 600°C), (>10h, 550°C)
Chemical properties
Water   resistence	ISO719/DIN12111, HGB1 ISO720, HGA1
Acid   resistance	ISO1776/DIN12116, 1
Alkali   resistance	ISO695/DIN52322, A2
Optical   properties
Refractive   index	Nd: 1.47379
Transmittance (5mm)	>92%
Electrical   properties
Specific   resistance  1g	250°C, 8.0Ω×cm
Dielectric loss	Tan , 38×(10)-4
Dielectric Constant	4.7
Chemical   component
SiO2	79-82%
B2O3	8-14%
Na2O	2-4%
Al2O3	1-6%